Diffusion Alloy Powder
Click image to view full size image
Product: Views:95Diffusion Alloy Powder 
Unit price: Negotiable
MOQ:
Quantity:
Delivery date: Since the payment date Days delivery
Valid until: Long-term effective
Last updated: 2019-07-02 00:28
  Inquiry
Details

LAP100.29D1: Add Ni(1.70-2.10%)and Cu(1.60-1.90%)in to the base powder(LAP100.29Mo1)mix uniformly. It enables the powder has high compressibility, stable dimensional change rate and good sintering performance. It is suitable for production of high strength materials.

·The powder has high compressibility and high strength.

·By adding superfine Cu powder improves powders uniformity and stability.

·Suitable for production of high strength and high dimensional precision high quality PM parts.


Product standard and content(wt%)
Composition Fe C S Si Mn P O Mo Cu Ni
Standard balance ≤0.015 ≤0.015 ≤0.05 ≤0.15 ≤0.015 ≤0.15 0.5-0.7 1.6-1.9 1.7-2.1
Classic - 0.006 0.008 0.03 0.1 0.01 0.11 0.52 1.72 1.75


Sieve analysis (particle size distribution)

um 180 180/150 150/106 106/75 75/45 -45
wt% trace ≤1 balance balance balance 10-30
Classic 0 0.3 16.5 25 30.2 20.8





Properties

LAP100.29D1+0.3%C+0.6%Zn-st, condition: temperature1120℃, sintering time 30min.


LAP100.29D2: Add Ni(3.80-4.20%)and Cu(1.60-1.90%)into the base powder(LAP100.29Mo1) mix uniformly.Due to its high Ni content, it is suitable for production of high hardcnability and high strength parts.

·The powder has high compressibility and high strength.

·No segregation enables the stability of product's sintered size.

·The increase of Ni content improves the hardenability of the material.

·Suitable for the production of large parts which need heat treatment.


Product standard and content(wt%)
Composition Fe C S Si Mn P O Mo Cu Ni
Standard balance ≤0.015 ≤0.015 ≤0.05 ≤0.15 ≤0.015 ≤0.15 0.50-0.70 1.60-1.90 3.80-4.20
Classic - 0.005 0.008 0.02 0.1 0.011 0.1 0.52 1.75 3.85


Sieve analysis (particle size distribution)

μm 180 180/150 150/106 106/75 75/45 -45
wt% trace ≤1 balance balance balance 10-30
Classic 0 0.7 19.7 25.7 31.8 22.1







Properties

LAP100.29D2+0.3%C+0.6%Zn-st, condition: temperature1120℃, sintering time 30min.


Package and delivery

1000kg per big flexbag and 25kg per small bag packed into one big bag




Application

This type of metal powder can be used for the material of powder metallurgy sinter component parts.